The analysis and fabrication of a novel tin-nickel mixed salt electrolytic coloured processing and the performance of coloured films for Al-12.

Shang, Yan; Liu, Changsheng; Fernandez, Carlos; Rajendran, L.; Kirthiga, M.; Wang, Yuhong; Niu, Dun; Liu, Dongdong; Wang, Linshan

Authors

Yan Shang

Changsheng Liu

Carlos Fernandez

L. Rajendran

M. Kirthiga

Yuhong Wang

Dun Niu

Dongdong Liu

Linshan Wang

Abstract

We present for the first time the analysis and fabrication of a novel Tin-Nickel mixed salt electrolytic coloured processing and the performance of coloured films for Al-12.7Si-0.7Mg alloy. This alloy is a novel alloy containing high silicon aluminum alloy extrusion profile which presents excellent mechanical properties as well as broad market prospects. Nevertheless, this kind of material is urgent in need of surface treatment technology. The orthogonal design and single factor tests were applied to optimize for electrolytic coloured technological conditions. By controlling operation conditions, the uniform electrolytic coloured films with different color were obtained. Analysis of microstructure showed that tin particles had been deposited in the coloured film. The coloured films, about 10 mu m thick, were uniform, dense and firmly attached to the substrate. After the coloured samples were maintained at 400AC for 1 h, or quenched from 300AC to room temperature, the coloured films did not change, demonstrating excellent thermostability and thermal shock resistance. Acid and alkali corrosion tests and potentiodynamic polarization showed that corrosion resistance of coloured sample was much better than those of untreated samples. After 240 h neutral salt spray test, protection ratings and appearance ratings of coloured films were Grade 9.

Journal Article Type Article
Publication Date Jan 31, 2017
Journal International journal of precision engineering and manufacturing
Print ISSN 1229-8557
Publisher New Publisher Required
Peer Reviewed Peer Reviewed
Volume 18
Issue 1
Pages 93-98
Institution Citation SHANG, Y., LIU, C., FERNANDEZ, C., RAJENDRAN, L., KIRTHIGA, M., WANG, Y., NIU, D., LIU, D. and WANG, L. 2017. The analysis and fabrication of a novel tin-nickel mixed salt electrolytic coloured processing and the performance of coloured films for Al-12.7Si-0.7Mg alloy in acidic and alkali corrosive environments. International journal of precision engineering and manufacturing [online], 18(1), pages 93-98. Available from: https://doi.org/10.1007/s12541-017-0011-x
DOI https://doi.org/10.1007/s12541-017-0011-x
Keywords Al-12.7-Si-0.7-Mg alloy; Tin nickel mixed salt; Electrolytic coloured; Performance; Corrosion resistance

Files




You might also like


Downloadable Citations